sd zinc primer 2000 無機富鋅底漆2000

product description

產(chǎn)品簡介

a self-curing inorganic zinc coating based on alkyl silicate binder

烷基硅酸酯為基料的自干型無機富鋅涂料

recommended use

用途

compatible with blasted steel surfaces and inorganic zinc shop-primed surfaces

適用于預(yù)處理后的鋼材及無機富鋅車間底漆表面

complied standards

符合標準

complies with iso 12944-5、sspc paint 20、hg/t 3668-2009

符合iso 12944-5、sspc paint 20、hg/t 3668-2009 富鋅底漆中的成分要求

features

產(chǎn)品特性

remarkable corrosion resistance

極好的防腐性能

outstanding resistance to impact, mechanical abrasion and organic solvent

優(yōu)良的耐沖擊、耐磨損和耐有機溶劑性能

excellent initial hardness

極好的初始硬度

high-build applicability

極好的厚涂施工性能

remarkable heat resistance and less scorch by heat treatment

優(yōu)良的耐熱性，熱處理燒損少

physicalproperties

基本數(shù)據(jù)

color

顏色

volume solids

體積固體份

voc

揮發(fā)性有機化合物含量

flash point

閃點

film thickness

涂裝膜厚

theoretical coverage

理論涂布率

grey

灰色

60%

402g/l，accord with eu dircrtive2004/42/ec，subcategory j

402g/l，符合歐盟溶劑排放指令2004/42/ec，j 子類別

greater than 19℃

19℃以上

dry : 60-75 microns/coat wet : 100-125microns/coat

干膜: 60-75 微米/道濕膜:100-125 微米/道

0.373kg/m2/75microns

0.373 千克/平方米/75 微米

practical coverage depending on surface conditions, environment, applications, etc.

實際涂布率與表面處理, 外界環(huán)境, 施工方法等多種因素有關(guān)。

application

施工

application temperature

施工溫度

mixing

混合

mixing ratio

混合比例

pot life

混合使用期

5℃-40℃

add powder to liquid first, then mix thoroughly with power agitator

將粉末加入液體，使用動力工具攪拌均勻

liquid/powder=20/86(by weight)

液體粉末=20/86（重量比）

5℃ 10℃ 20℃ 30℃

8hrs 7hrs 6hrs 5hrs

application methods

施工方法

thinner

稀釋劑

drying time &

overcoating interval

干燥時間&涂裝間隔

applied substrates

適用底材

typical topcoat

適用上涂

airless spray, air spray

無氣噴涂、空氣噴涂

airless spray 無氣噴涂

nozzle tip 噴嘴尺寸0.43mm-0.53mm

nozzle pressure 出口壓力≥10mpa

thinning ratio 稀釋比率0-10% by weight（重量比）

sd zinc 2000primer thinner

專用稀釋劑

temperature 溫度5℃ 20℃ 30℃

surface dry 指觸干燥60mins 30mins 30mins

touch dry 半硬干燥6hrs 3hrs 1hr

min. interval Zui小涂裝間隔48hrs 48hrs 48hrs

max. interval Zui大涂裝間隔

bare steel

裸鋼

epomarine sealer primer or according to the coating system of cosco kansai.

環(huán)氧連接漆或參考我司涂裝配套