石墨電極（np,hp）

石墨電極主要用于電爐煉鋼及礦熱電爐和電阻爐。通過石墨電極導(dǎo)入電流，在電爐熔煉區(qū)內(nèi)產(chǎn)生電弧，升溫2000℃左右進行冶煉。我公司石墨電極系列產(chǎn)品適用于普通電爐和高電壓短電弧的大功率電爐。

graphiteelectrode is mainly usde for steel-making in electricfurnace,mineral hot furnace and electric resistancefurnace.graphite electrode conducts electric current into thefurnace.electric current produces arc in the smelting district inthe electric furnace,when the temperature increase to about2000℃,smelting begins.our a series ofgraphite electrode is applicable to the common furnace and highpower furnace with high pressure and shortarc.

普通功率石墨電極：

specificationsand properties:

比電阻(resistivity)6-9μωm，

抗折強度(bendingstrength)10-12mpa，

彈性模量(elasticmodulus)7-9gpa，

熱膨脹系數(shù)(cte)1.8-2.9x10-6/℃，

抗壓強度(compressivestrength18)18-22 mpa，

體積密度(bulkdensity)1.52-1.57g/cm3,

灰分(ash)0.3％。

2.直徑(dia)400-500mm，

比電阻(resistivity)7-10μωm，

抗折強度(bendingstrength)6.5-10mpa，

彈性模量(elasticmodulus)7-9.3gpa，

熱膨脹系數(shù)(cte)1.7-2.9x10-6/℃，

抗壓強度(compressivestrength)18-22 mpa，

體積密度(bulkdensity)1.52-1.57g/cm3,

灰分(ash)0.3％。

高功率石墨電極：

hp graphiteelectrode

1.直徑(dia)200-350mm，

比電阻(resistivity)6-7μωm，

抗折強度(bendingstrength)10-15mpa，

彈性模量(elasticmodulus)9-12gpa，

熱膨脹系數(shù)(cte)1.6-2.2x10-6/℃，

抗壓強度(compressivestrength)24-28 mpa，

體積密度(bulkdensity)1.62-1.70g/cm3,

灰分(ash)0.3％。

2.直徑(dia)400-500mm，

比電阻(resistivity)6-7μωm，

抗折強度(bendingstrength)10-13mpa，

彈性模量(elasticmodulus)9-12gpa，

熱膨脹系數(shù)(cte)1.5-2.2x10-6/℃，

抗壓強度(compressivestrength)24-26 mpa，

體積密度(bulkdensity)1.62-1.68g/cm3,

灰分(ash)0.3％。

電極接頭：

graphite electrodenipple:

直徑(dia)200-500mm，

比電阻(resistivity)4-7μωm，

抗折強度(bendingstrength)12-20mpa，

彈性模量(elasticmosulus)12-14gpa，

熱膨脹系數(shù)(cte)2.0-3.0x10-6/℃，

抗壓強度(compressivestrength)32-38 mpa，

體積密度(bulkdensity)1.70-1.80g/cm3,

灰分(ash)0.3％。