物性參數(shù)大全旭化成PA66（1300S）特性高流動;高剛性;良好的柔韌性應(yīng)用領(lǐng)域連接器;汽車領(lǐng)域;配件;消費品領(lǐng)域物理性能測試條件測試方法測試結(jié)果單位密度 /比重干ASTM D-7921.14
ASTMD7921.14g/cm3收縮率MD2.0mmASTMD9951.3%TD2.0mmASTMD9952.0%干旭化成方法1.3-2.0%吸水率(23°C,24hr)ASTMD5702.5%機械性能測試條件測試方法測試結(jié)果單位斷裂伸長率23°CASTMD63850%
ASTM D638/ISO 52750%斷裂延伸率干(濕)ASTM D-63850(250)%抗撓強度干(濕)ASTMD-790118(54)Mpa抗撓系數(shù)干(濕)ASTM D-7902.8(1.2)GPa拉伸強度干(濕)ASTMD-63879(57)Mpa23°CASTMD63879Mpa洛氏硬度干(濕)ASTM D-78580(55)MScale干(濕)ASTM D-785120(108)R scale磨耗率濕ASTM D-10447
彎曲模量
ASTM D790/ISO1782790kg·cm/cm(J/M)ft·lb/in23°CASTMD7902800Mpa彎曲強度23°CASTMD790118Mpa
ASTM D790/ISO178118kg·cm/cm(J/M)ft·lb/in懸壁梁缺口沖擊強度23°CASTMD25639J/m懸臂梁式缺口沖擊強度干(濕)ASTMD-25639(147)J/mCharpy沖擊強度
ASTM D256/ISO 17939kg·cm/cm(J/M)ft·lb/in熱性能測試條件測試方法測試結(jié)果單位比熱容干
1670J/(kg.k)導(dǎo)熱率干
0.2W/(m.K)燃燒性（率）
UL94v-2
熱變形溫度0.45MPa未退火ASTMD648230°C1.80MPa未退火ASTMD64870°C0.46MPa,干ASTMD-648230℃1.82MPa,干ASTM D-64870℃
ASTM D648/ISO 75230℃（℉）線膨脹系數(shù)比熱
1670J/kg/°C導(dǎo)熱系數(shù)JISR26180.2W/m/K線性膨脹系數(shù)
ASTM D696/ISO 113598mm/mm.℃干ASTM D-6968
阻燃性干UL 94V-2
電氣性能測試條件測試方法測試結(jié)果單位耗散因數(shù)相對漏電起痕指數(shù)ASTMD3638600V絕緣強度
ASTMD14920KV/mm體積電阻率
ASTM D257/IEC6009310-10Ω.cm可燃性(Flammability)測試條件測試方法測試結(jié)果單位防火等級氧指數(shù)ASTM286326%
UL-940.40mmV-2
UL-940.71mmV-2
UL-941.50mmV-2
UL-943.00mmV-2硬度Hardness測試條件測試方法測試結(jié)果單位洛氏硬度
ASTMD785120R
ASTMD78580M（Scale）物性性能測試條件測試方法測試結(jié)果單位比重（密度）
ASTM D792/ISO 11831.14
吸水率 23℃/24H
ASTM D570/ISO 622.5%基本性能測試條件測試方法測試結(jié)果單位吸濕率濕
2.5%其他性能測試條件測試方法測試結(jié)果單位氧指數(shù)干ASTM D-286326%